SABIC® LDPE PCG09
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sUPGGx_SABICLDPEPCG09.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Low density polyethylene for Healthcare Description SABIC® LDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® LDPE PCG09 is an additive free grade, typically designed for healthcare packaging and can typically be converted by Injection Molding and Cast Film to produce caps and closures, small bottles and secondary packaging. Compliance to Regulations SABIC® LDPE PCG09 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 7.5 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 25 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 10.0 | cm³/10min | ISO 1133 |
| 190°C/5.0 kg | 33.0 | cm³/10min | ISO 1133 |
| Environmental Stress-Cracking Resistance (60°C, 3.00mm, Rhodacal-DS10, injection molding) | 1.00 | hr | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1(Shore D, Injection Molded) | 41 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2(Injection Molded) | 170 | MPa | ISO 527-2/1A/50 |
| Tensile Stress 3 | ISO 527-2/1A/50 | ||
| Yield, injection molding | 9.00 | MPa | ISO 527-2/1A/50 |
| Fracture, injection molding | 10.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain 4(Break, Injection Molded) | 100 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 5 | ISO 180/A | ||
| -30°C, injection molding | 8.0 | kJ/m² | ISO 180/A |
| 23°C, injection molding | 50 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(0.45 MPa, Unannealed) | 46.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature 7 | 93.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 110 | °C | DIN 53765 |
| Enthalpy Change | 138 | J/g | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | Conditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 2 . | Conditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 3 . | Conditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 4 . | Conditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 5 . | Conditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 6 . | Conditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 7 . | Conditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AECN Noir 03 TL | Arkema | Nylon 12 | Rilsamid® |
| Melinex® 994 | DuPont Teijin Films U.S. | Polyester, TP | Melinex® |
| Keliren® CM421 | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| LUVOCOM® 80-8604/EM/BL | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Sylvin 8470-70 Green 3174 | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |