SABIC® HDPE B6246
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sUAbv5_SABIC-HDPE-B6246.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® HDPE B6246 is developed for thin walled packaging processed at high production speed. This grade is suitable for packaging of milk, yoghurt, fruit juice and is suitable in extrusion applications for profiles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.962 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.50 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 46 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 2.5 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance 1(75°C, 1.00 mm, Rhodacal-DS10, Compression Molded) | 5.00 | hr | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (15 seconds, molded) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1300 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 29.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 18.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C, molded | 7.0 | kJ/m² | ISO 180/1A |
| 23°C, molded | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 89.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 128 | °C | ISO 306/A50 |
| Melting Temperature | 135 | °C | DIN 53765 |
| Enthalpy Change | 225 | J/g | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | 3 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E595 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Telene® 1811 A/B | Telene S.A.S., a Rimtec Corporation company | DCPD | Telene® |
| Yuyao PA 011BG30 | Yuyao Tenglong Plastics Co., Ltd. | Nylon 66/6 | Yuyao PA |
| ENSOFT SD-760-65A | ENPLAST, a Ravago Group Company | TPE | ENSOFT |
| Sylvin 9915-72 White 1538 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |