LG ASA LI911
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sU9AYf_LG-ASA-LI911.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Good Weatherability, High Flow Applications Air-Conditioner grill, sewing machine cover, Electric/Electronic Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2170 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20 mm | > 6.0 | % | |
| Break | 20 | % | |
| Flexural Modulus 4(3.20 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 3.20 mm) | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 29 | J/m | |
| -30°C, 6.40 mm | 29 | J/m | |
| 23°C, 3.20 mm | 140 | J/m | |
| 23°C, 6.40 mm | 120 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 6.40 mm | 96.0 | °C | |
| 1.8 MPa, Annealed, 6.40 mm | 87.0 | °C | |
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | > 0.010 | % | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 210 to 220 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Back Pressure | 0.490 to 0.981 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ C18UST4LSR | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| NYLOY® UB-0010N G50L1N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| ADDILENE H 420 K24 | ADDIPLAST | PP Homopolymer | ADDILENE |
| Evoprene™ CE 6185 | AlphaGary | TPE | Evoprene™ CE |
| Globalprene® 7533 | Lee Chang Yung Chemical Industry Corp. | SEBS | Globalprene® |