VITAMIDE® AK20BK6424
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sTRNiY_VITAMIDE-AK20BK6424.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® AK20BK6424 is a Polyamide 66 (Nylon 66) product. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption | |||
| 24 hr | 1.3 | % | ASTM D570 |
| 23°C, 24 hr | 1.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Break | 90.0 | MPa | ISO 527-2 |
| -- | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3100 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 120 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 5.00 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 | |
| Notched Izod Impact Strength | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 200 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 28 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 600 | V | IEC 60112 |
| -- | 600 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL6F 809-HSB | Marco Polo International, Inc. | LLDPE | MARPOL® |
| SABIC® PPcompound 8500 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Retpol® PDR 7386/3 UV3 | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| DOW™ HDPE DMDA-8910 NT 7 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| Karina YELLOW PVC COMPOUND 550D02/101-AT-IS (MECESA) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |