Category: | Nylon 6 , Polyamide 6 |
Manufacturer: | Wellman Engineering Resins |
Trademark: | Wellamid® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | sTQVYH_Wellamid-MRGF30-10-42H-NBK1.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Wellamid® MRGF30/10 42H-NBK1 is a Polyamide 6 (Nylon 6) material filled with 40% glass\mineral. It is available in Asia Pacific, Europe, Latin America, or North America. Primary attribute of Wellamid® MRGF30/10 42H-NBK1: Flame Rated. Typical application of Wellamid® MRGF30/10 42H-NBK1: Automotive |
General Information | |
---|---|
Filler / Reinforcement |
|
Forms |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.49 | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow : 23°C | 0.80 to 1.2 | % | |
Flow : 23°C | 0.20 to 0.60 | % |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress (Yield, 23°C) | 95.0 | MPa | ISO 527-2 |
Tensile Strain (Yield, 23°C) | 3.0 | % | ISO 527-2 |
Flexural Modulus (23°C) | 9000 | MPa | ISO 178 |
Flexural Stress (23°C) | 145 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature (1.8 MPa, Unannealed) | 195 | °C | ISO 75-2/A |
Melting Temperature (DSC) | 220 | °C | ISO 3146 |
Flammability | Nominal Value | Test Method | |
---|---|---|---|
Flame Rating (0.750 mm) | HB | UL 94 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
SUSTASON PES | Röchling Sustaplast SE & Co. KG | PESU | SUSTASON |
Taitacell EPS 321F | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
ADPOLY BP-402 | Lotte Chemical Corporation | PP, Unspecified | ADPOLY |
Latilub 52/30-15T G/30 | LATI S.p.A. | PP Homopolymer | Latilub |
TECACOMP® PA66 TC black 4022 | Ensinger GmbH | Nylon 66 | TECACOMP® |