AvaSpire® AV-630
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | AvaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sT2kl0_AvaSpire-AV-630.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AvaSpire AV -630 is unreinforced polyaryletherketone (PAEK), which is used to replace low-fluidity PEEK (polyetheretherketone) for ultra-thin film extrusion. Films with a thickness as low as 0.2 mils (5 microns) can be successfully melted and extruded by conventional thermoplastic film extrusion equipment with AV -630. Compared with the corresponding PEEK film, the AV-630 film has certain performance advantages, including better toughness and ductility, higher mechanical integrity when the temperature is higher than 150 ℃, better adaptability to adhesives, and more resistance to flame propagation. Ultra-thin films (thickness <15 microns) also show better toughness. Under the same thickness, the hand feel is smoother than PEEK film. Submil thickness films produced by AV -630 can be widely used in various industrial fields. Conventional applications include capacitors, electrical insulation, flexible circuit substrates, special laminates, composite film layers, moisture barriers, linings and aerospace films, such as thermal insulation blanket bagging materials. -natural color: AvaSpire AV-630 NT |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3300 | MPa | ASTM D638 |
| -- | 3400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Yield | 89.0 | MPa | ISO 527-2/1A/50 |
| -- 2 | 92.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield 3 | 6.0 | % | ASTM D638 |
| Yield | 5.4 | % | ISO 527-2/1A/50 |
| Fracture 4 | 50 - 80 | % | ASTM D638 |
| Fracture | 50 - 80 | % | ISO 527-2/1A/50 |
| Flexural Modulus | |||
| -- | 320 | MPa | ASTM D790 |
| -- | 3300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 127 | MPa | ASTM D790 |
| -- | 128 | MPa | ISO 178 |
| Compressive Strength | 110 | MPa | ASTM D695 |
| Shear Strength | 79.0 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 91 | J/m | ASTM D256 |
| -- | 7.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | No Break | ASTM D4812, ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(1.8 MPa, Annealed, 3.20 mm) | 181 | °C | ASTM D648 |
| Glass Transition Temperature | 158 | °C | ASTM D3418 |
| Peak Melting Temperature | 340 | °C | ASTM D3418 |
| Specific Heat | DSC | ||
| 50°C | 1390 | J/kg/°C | DSC |
| 200°C | 1960 | J/kg/°C | DSC |
| Thermal Conductivity | 0.23 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.9E+17 | ohms | ASTM D257 |
| Volume Resistivity | 6.2E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (0.0600mm, amorphous film) | 180 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 38 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr |
| Extrusion instructions |
|---|
| 干燥： - AvaSpire AV -630树脂必须在熔融加工前，彻底干燥。否则，成型部件表面容易形成条纹甚至严重起泡等程度不同的缺陷。塑料粒子可以在循环空气烘箱中的托盘或除湿料斗干燥机上干燥。干燥条件建议：150 ℃（300 °F）温度下4小时。 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 200°C,2 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 307 TFE 12 | RTP Company | PC | RTP |
| Amilan® CM8000 | Toray Resin Company | Nylon Copolymer | Amilan® |
| AT 525 | Celanese EVA Performance Polymers | LDPE | AT |
| Plaslube® ABS 8004 | Techmer Engineered Solutions | ABS | Plaslube® |
| Sylvin 4222-90LG Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |