VESTAMID® HTplus M1035
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® HTplus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sT0p3U_VESTAMID-HTplus-M1035.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
VESTAMID HTplus M1035 is a glass-fiber reinforced (50%), heat-stabilized polyphthalamide compound (PPA) for injection molding. This base resin is especially suitable for manufacturing parts subjected to high temperature. VESTAMID HTplus M1035 is supplied as cylindrical pellets in polyethylene packaging. Drying at 120°C for at least 4 hours before processing is recommended. For information about processing of VESTAMID HTplus M1035, please follow the general recommendations for PPA in our information "Handling and Processing of VESTAMID HTplus." |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.64 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 250 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 16000 | MPa | ISO 178 |
| Flexural Stress | 360 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Complete Break | 14 | kJ/m² | |
| 23°C, Complete Break | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C, Complete Break | 50 | kJ/m² | |
| 23°C, Complete Break | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 313 | °C | ISO 306/A |
| -- | 289 | °C | ISO 306/B |
| Melting Temperature | 300 to 315 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 20°C | 2.7E-5 | cm/cm/°C | |
| Transverse : 20°C | 2.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 66 Prime Series PXIM-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Geon™ Vinyl Dry Blend E6755 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |
| LAPEROS® S150 | Polyplastics Co., Ltd. | LCP | LAPEROS® |
| KumhoSunny PBT 3730FG-NH | Shanghai KumhoSunny Plastics Co., Ltd. | PBT | KumhoSunny PBT |
| Sylvin 8225-80FR Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |