Generic Nylon 6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sRunIW_Generic-Nylon-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.902 - 1.42 | g/cm³ | ASTM D792 |
| 23°C | 1.09 - 1.18 | g/cm³ | ISO 1183 |
| -- | 1100 | kg/m³ | ISO 1183 1 |
| -- | 1.09 - 1.26 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | |||
| 235°C/1.0 kg | 0.90 - 5.0 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 2.7 - 16 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 3.00 - 176 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.79 - 1.8 | % | ASTM D955 |
| Transverse flow : 23°C | 1.1 - 2.0 | % | ASTM D955 |
| 23°C | 0.84 - 2.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.53 - 2.0 | % | ASTM D570 |
| 23°C, 24 hr | 0.64 - 2.6 | % | ISO 62 |
| Saturated, 23°C | 0.10 - 9.6 | % | ASTM D570 |
| Saturated, 23°C | 6.8 - 10 | % | ISO 62 |
| Saturation | 9.2 | % | ISO 62 2 |
| Equilibrium, 23°C | 0.38 - 3.1 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.4 - 3.1 | % | ISO 62 |
| Balance | 2.7 | % | ISO 62 3 |
| K-Value (23°C) | 75.9 - 80.0 | ISO 1628-2 | |
| Viscosity Number | 115 - 249 | cm³/g | ISO 307 |
| Relative Viscosity | 2.4 - 4.2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 104 - 121 | ASTM D785 | |
| 23°C | 89 - 121 | ISO 2039-2 | |
| Durometer Hardness | |||
| 23°C | 64 - 81 | ASTM D2240 | |
| 23°C | 59 - 82 | ISO 868 | |
| Ball Indentation Hardness | 36.0 - 162 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 739 - 3810 | MPa | ASTM D638 |
| 23°C | 100 - 6710 | MPa | ISO 527-2 |
| -- | 4310 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield, 23°C | 32.7 - 93.0 | MPa | ASTM D638 |
| Yield, 23°C | 25.0 - 90.0 | MPa | ISO 527-2 |
| Yield | 64.5 | MPa | ISO 527-2 5 |
| Fracture, 23°C | 39.2 - 112 | MPa | ASTM D638 |
| Fracture, 23°C | 30.2 - 153 | MPa | ISO 527-2 |
| Fracture | 95.0 | MPa | ISO 527-2 6 |
| Limit, 23°C | 47.5 - 81.3 | MPa | ASTM D638 |
| 23°C | 43.4 - 88.8 | MPa | ASTM D638 |
| 23°C | 38.8 - 151 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 0.55 - 11 | % | ASTM D638 |
| Yield, 23°C | 0.87 - 26 | % | ISO 527-2 |
| Yield | 12 | % | ISO 527-2 7 |
| Fracture, 23°C | 0.40 - 110 | % | ASTM D638 |
| Fracture, 23°C | 0.40 - 50 | % | ISO 527-2 |
| Fracture | 4.9 - 6.4 | % | ISO 527-2 8 |
| Nominal Tensile Strain at Break (23°C) | 2.8 - 55 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 5050 | MPa | ISO 899-1 |
| 1000 hr | 3330 | MPa | ISO 899-1 |
| Flexural Modulus | |||
| 23°C | 562 - 3390 | MPa | ASTM D790 |
| 23°C | 502 - 6000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 33.7 - 125 | MPa | ASTM D790 |
| 23°C | 18.3 - 211 | MPa | ISO 178 |
| Yield, 23°C | 34.5 - 122 | MPa | ASTM D790 |
| Fracture, 23°C | 37.2 - 194 | MPa | ASTM D790 |
| Compressive Modulus | 2150 - 2510 | MPa | ASTM D695 |
| Compressive Strength | |||
| 23°C | 9.80 - 111 | MPa | ASTM D695 |
| 23°C | 21.0 - 122 | MPa | ISO 604 |
| Shear Strength (23°C) | 57.2 - 76.5 | MPa | ASTM D732 |
| Coefficient of Friction | 0.040 - 1.4 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 3.50 - 10.1 | mg | ASTM D1044 |
| Deformation Under Load (23°C) | 0.510 - 1.52 | % | ASTM D621 |
| Wear Factor | 22 - 210 | 10^-8 mm³/N·m | ASTM D3702 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 - 51 | µm | |
| secant modulus | |||
| MD | 615 - 3100 | MPa | ASTM D882 |
| TD | 648 - 2800 | MPa | ASTM D882 |
| 23°C | 450 - 490 | MPa | ISO 527-3 |
| Tensile Strength | |||
| MD : Yield | 26.5 - 98.1 | MPa | ASTM D882 |
| Yield, 23°C | 30.0 - 40.0 | MPa | ISO 527-3 |
| MD : Fracture | 58.6 - 276 | MPa | ASTM D882 |
| TD : Fracture | 252 - 345 | MPa | ASTM D882 |
| Fracture, 23°C | 83.0 - 100 | MPa | ISO 527-3 |
| 23°C | 80.0 - 96.0 | MPa | ISO 527-3 |
| Tensile Elongation | |||
| Yield, 23°C | 7.0 - 15 | % | ISO 527-3 |
| MD : Fracture | 56 - 100 | % | ASTM D882 |
| TD : Fracture | 70 - 92 | % | ASTM D882 |
| Fracture, 23°C | 340 - 700 | % | ISO 527-3 |
| Elmendorf Tear Strength | |||
| MD | 19 - 130 | g | ASTM D1922 |
| -- | 10 - 15 | N | ISO 6383-2 |
| Trouser Tear Resistance | 23.0 - 50.0 | N/mm | ISO 6383-1 |
| Oxygen Permeability (23°C) | 0.028 - 2.0 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Oxygen Transmission Rate (23°C) | 15 - 40 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate | 14 - 35 | g/m²/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 39.2 - 53.0 | J/m | ASTM D256 |
| 23°C | 1.5 - 31 | kJ/m² | ISO 179 |
| -30°C | 4.69 | kJ/m² | ISO 179/1eA 9 |
| 23°C | 42.0 | kJ/m² | ISO 179/1eA 10 |
| Charpy Unnotched Impact Strength | |||
| 23°C | 48 - 120 | kJ/m² | ISO 179 |
| 23°C | 82.3 | kJ/m² | ISO 179/1eU 11 |
| Notched Izod Impact | |||
| 23°C | 42 - 150 | J/m | ASTM D256 |
| 23°C | 2.5 - 25 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 32 - 1600 | J/m | ASTM D256 |
| 23°C | 41 - 100 | kJ/m² | ISO 180 |
| Multi-Axial Instrumented Impact Energy (23°C) | 2.00 - 67.2 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 1230 - 5140 | N | ISO 6603-2 |
| Dart Drop Impact (23°C) | 35.3 - 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 146 - 219 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 50.9 - 216 | °C | ISO 75-2/B |
| 0.45 MPa | 185 | °C | ISO 75-2 12 |
| 1.8 MPa, not annealed | 45.8 - 83.4 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 49.5 - 82.8 | °C | ISO 75-2/A |
| 1.8 MPa | 62.4 | °C | ISO 75-2 13 |
| 8.0 MPa, not annealed | 40.0 - 45.0 | °C | ISO 75-2/C |
| Continuous Use Temperature | 69.8 - 180 | °C | ASTM D794 |
| Vicat Softening Temperature | |||
| -- | 170 - 225 | °C | ASTM D1525 |
| -- | 196 - 209 | °C | ISO 306 |
| Ball Indentation Temperature | 169 - 170 | °C | IEC 60598-1 |
| Melting Temperature | |||
| -- | 211 - 220 | °C | |
| -- | 217 - 226 | °C | DSC |
| -- | 217 - 222 | °C | ISO 11357-3 |
| -- | 215 - 221 | °C | ASTM D3418 |
| -- | 220 - 223 | °C | ISO 3146 |
| Peak Crystallization Temperature (DSC) | 216 - 220 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | |||
| Flow | 2.8E-5 - 1.1E-4 | cm/cm/°C | ASTM D696 |
| Flow | 3.9E-5 - 1.0E-4 | cm/cm/°C | ASTM E831 |
| Flow | 5.5E-5 - 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.6E-5 - 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1670 - 1680 | J/kg/°C | ASTM C351 |
| Thermal Conductivity (23°C) | 0.23 - 0.30 | W/m/K | ASTM C177, ISO 8302 |
| RTI Elec | 65.0 - 130 | °C | UL 746 |
| RTI Imp | 65.0 - 106 | °C | UL 746 |
| RTI | 65.0 - 121 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.5E+15 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | |||
| 23°C | 10 - 2.5E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0 - 2.5E+16 | ohms·cm | IEC 60093 |
| -- | 1.0E+10 - 1.0E+13 | ohms·m | IEC 60093 14 |
| Dielectric Strength | |||
| 23°C | 12 - 39 | kV/mm | ASTM D149 |
| 23°C | 18 - 37 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.80 - 3.75 | ASTM D150 | |
| 23°C | 3.33 - 7.18 | IEC 60250 | |
| 23°C | 4.87 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.020 - 0.30 | ASTM D150 | |
| 23°C | 1.0E-3 - 0.35 | IEC 60250 | |
| 1 MHz | 0.13 | IEC 60250 15 | |
| Arc Resistance | 114 - 195 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 495 - 600 | V | UL 746 |
| Comparative Tracking Index | |||
| -- | 586 - 600 | V | IEC 60112 |
| -- | 594 - 600 | V | ASTM D3638 |
| Insulation Resistance (23°C) | 1.0E+10 - 1.0E+12 | ohms | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | |||
| -- | 30 | % | ASTM D2863 |
| -- | 21 - 32 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 113 - 170 | ASTM D2457 | |
| Transmittance | 82.9 - 85.0 | % | ASTM D1003 |
| Haze | 0.50 - 5.0 | % | ASTM D1003 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 380 - 2740 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 82.5 | °C | |
| Drying Time | 2.0 - 5.3 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Max Moisture | 0.095 - 0.20 | % | |
| Suggested Shot Size | 50 - 55 | % | |
| Suggested Max Regrind | 30 | % | |
| Hopper Temperature | 60.0 - 240 | °C | |
| Rear Temperature | 223 - 276 | °C | |
| Middle Temperature | 232 - 283 | °C | |
| Front Temperature | 245 - 290 | °C | |
| Nozzle Temperature | 149 - 277 | °C | |
| Processing (Melt) Temp | 239 - 290 | °C | |
| Mold Temperature | 59.0 - 90.1 | °C | |
| Injection Pressure | 6.89 - 97.4 | MPa | |
| Holding Pressure | 32.5 - 75.0 | MPa | |
| Back Pressure | 0.172 - 1.27 | MPa | |
| Screw Speed | 45 - 125 | rpm | |
| Clamp Tonnage | 4.0 - 7.0 | kN/cm² | |
| Cushion | 3.97 - 4.80 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 6This information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 - 82.5 | °C | |
| Drying Time | 2.9 - 9.2 | hr | |
| Suggested Max Moisture | 0.056 - 0.20 | % | |
| Cylinder Zone 1 Temp. | 216 - 257 | °C | |
| Cylinder Zone 2 Temp. | 244 - 248 | °C | |
| Cylinder Zone 3 Temp. | 229 - 260 | °C | |
| Cylinder Zone 4 Temp. | 245 - 247 | °C | |
| Cylinder Zone 5 Temp. | 241 - 247 | °C | |
| Adapter Temperature | 263 - 264 | °C | |
| Melt Temperature | 234 - 266 | °C | |
| Die Temperature | 232 - 260 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 6This information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 13 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 14 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 15 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9713-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VITAMIDE® AR34NT6525 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Hanwha Total PE R908U | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| Kumho KBR 710H | Korea Kumho Petrochemical Co., Ltd. | PBR, Low Cis | Kumho KBR |
| LIHAN® A705H | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |