Celstran® PP-GF20-03 natural
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sRZyHk_CelstranPPGF2003natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer reinforced with 20 weight percent long glass fibers. The fibers are chemically coupled to the polyproylene matrix. Then pellets are cylindrical and normally as well as the embedded fibers 10mm long Developed for aesthetic applications requirering good impact with a class A appearance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.70 | % | ISO 294-4 |
| Flow | 0.47 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 105 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 5150 | MPa | ISO 178 |
| Flexural Stress (23°C) | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 23 | kJ/m² | ISO 179/1e |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 157 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 220 - 230 | °C | |
| Middle Temperature | 230 - 240 | °C | |
| Front Temperature | 240 - 250 | °C | |
| Nozzle Temperature | 240 - 250 | °C | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 30 - 70 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Feed Temperature: 20 to 50°CZone 4 Temperature: 250°CManifold Temperature: 230 to 270°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S-RIM™ 6260 Black | Hapco Inc. | TP, Unspecified | S-RIM™ |
| Bergamid™ B700 G15 H BK041 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| LG PMMA ID158 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| LNP™ THERMOCOMP™ EC006 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| Edgetek™ PC-10GF/15T BK029 | PolyOne Corporation | PC | Edgetek™ |