Order Products : sales@su-jiao.com
SABIC® LDPE 2602H0W
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sR42eG_SABICLDPE2602H0W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2602H0W is a grade with very good optical properties. The grade contains no additives, has an increased density and shows a good draw down ability. The films are characterized by good mechanical properties. Application SABIC® LDPE 2602H0W is typically used for applications where enhanced stiffness is required. SABIC® LDPE 2602H0W can typically be used for food applications due to very low migration levels. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | > 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD | 250 | MPa | ISO 527-3 |
| TD | 260 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield | 13.0 | MPa | ISO 527-3 |
| TD : Yield | 13.0 | MPa | ISO 527-3 |
| MD : Fracture | 30.0 | MPa | ISO 527-3 |
| TD : Fracture | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture | > 300 | % | ISO 527-3 |
| TD : Fracture | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength | 150 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking | 10 | g | Internal method |
| Re-blocking | 30 | g | Internal method |
| Tear Strength | ISO 6383-2 | ||
| MD | 90.0 | kN/m | ISO 6383-2 |
| TD | 40.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 99.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 70 | ASTM D2457 | |
| Haze | 6.0 | % | ASTM D1003A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR WC 0587-21 BE1 RoHS | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| Quadrathane™ ALC-55D-B20 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| ALCUDIA® EVA PA-539 | REPSOL | EVA | ALCUDIA® EVA |
| Desmoderm® TXC EHC-01/1 | Covestro - PUR | PUR-Ester | Desmoderm® |
| PENTAMID AB S GV30 H natural | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |