Infino GP-8200G
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sQqRb4_Infino-GP-8200G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Material with the characteristic of dimensional stability and 20% GF that can be applied to pump and impeller housing |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/10.0 kg) | 7.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.38 to 0.46 | % | |
| Across Flow : 3.20 mm | 0.42 to 0.52 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 118 | ASTM D785 | |
| R-Scale | 121 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4900 | MPa | ASTM D638 |
| -- | 5500 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 100 | MPa | ASTM D638 |
| Yield | 120 | MPa | ISO 527-2/50 |
| Break 3 | 110 | MPa | ASTM D638 |
| Break | 120 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 4.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 5900 | MPa | ASTM D790 |
| -- 6 | 5900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 150 | MPa | ASTM D790 |
| -- 8 | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 120 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 110 | J/m | ASTM D256 |
| 23°C 10 | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 153 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 140 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 149 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 157 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 280 to 290 | °C | |
| Front Temperature | 300 to 310 | °C | |
| Nozzle Temperature | 310 | °C | |
| Mold Temperature | 50.0 to 100 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 406 | RTP Company | PS (GPPS) | RTP |
| Pro-fax RP311H | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| RheTech Thermoplastic Polyolefin FT1055-624 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Sindustris PP R7701 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| MARPOL® HDB 506 | Marco Polo International, Inc. | HDPE, MMW | MARPOL® |