Kinta FR6600
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kinta Technology (Hong Kong) Co., Ltd. |
| Trademark: | Kinta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sQf4wI_KintaFR6600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kinta FR6600 is a polyamide 66 (nylon 66) product,. It is available in the Asia-Pacific region. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.00 mm) | 0.50 - 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.1 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 80.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 12 | % | ASTM D638 |
| Flexural Modulus 3 | 3500 | MPa | ASTM D790 |
| Flexural Strength 4 | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 4.50 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 110 | °C | ASTM D648 |
| Melting Temperature | 265 | °C | DSC |
| CLTE - Flow | 2.0E-5 - 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dissipation Factor 5(23°C, 1 MHz) | 0.030 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 260 - 280 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Injection Pressure | 100 - 160 | MPa |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4183 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Pro-Comp™ PPBGF10-E | Southland Polymers | PP Impact Copolymer | Pro-Comp™ |
| Sinvicomp SGH2801 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Koylene ADL-CP AMR100NC | Reliance Industries Limited | PP Random Copolymer | Koylene ADL-CP |
| MAJ'ECO EFR150BS 9445 WHITE 3 | AD majoris | Biodeg Polymers | MAJ'ECO |