Innothane® IE-50AC
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sQWMbK_Innothane-IE-50AC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-50AC is a tough, abrasion resistant elastomer formulated for hand-batch processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. IE-50AC is particularly ideal for color-matching applications due to its transparent appearance. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.21 | g/cm³ | |
| Base Resin | 1.21 | g/cm³ | |
| Hardener | 1.23 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.40 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 50 Mix Ratio by Volume: 51 | ||
| Demold Time | 120 to 240 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.045 | Pa·s | |
| 25°C 2 | 0.88 | Pa·s | |
| 25°C 3 | 1.4 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 10 to 14 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 45 to 55 | ASTM D2240 | |
| Tensile Strength | 2.76 | MPa | ASTM D638 |
| Tensile Elongation at Break | 150 | % | ASTM D638 |
| Tear Strength | 17.5 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Keltan® 6951C | LANXESS Buna GmbH | EPDM | Keltan® |
| Kinta NB5010G | Kinta Technology (Hong Kong) Co., Ltd. | PC | Kinta |
| Xytron™ M6510A | DSM Engineering Plastics | PPS | Xytron™ |
| Sylvin 9604-95 Clear 896 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRILOY™ RX05497 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |