LNP™ LUBRICOMP™ AI001XXH compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sQ57Lg_LNP-LUBRICOMP-AI001XXH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* AI001XXH is a compound based on ABS resin containing 2% Silicone. Added features of this grade include: Healthcare, Wear Resistant. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 0.60 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.25 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.36 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2230 | MPa | ASTM D638 |
| -- | 2120 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 40.0 | MPa | ASTM D638 |
| Yield | 38.0 | MPa | ISO 527-2/5 |
| Break 3 | 32.0 | MPa | ASTM D638 |
| Break | 31.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.3 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2/5 |
| Break 5 | 44 | % | ASTM D638 |
| Break | 59 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2270 | MPa | ASTM D790 |
| -- 7 | 2120 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 56.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 60.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.46 | ||
| vs. Itself - Static | 0.43 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | -1.30 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 480 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 9 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1400 | J/m | ASTM D4812 |
| 23°C 10 | 130 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.40 | J | ASTM D3763 |
| -- | 3.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 86.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 86.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-2090-10A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Softflex® 7700 | Network Polymers, Inc. | TPE | Softflex® |
| Tarnoform® 300 CF2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Chemlon® 500 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Medalist® MD-53253 | Teknor Apex Company | TPE | Medalist™ |