KYNAR® 760 is a semi-crystalline high molecular weight pelletized polymer of vinylidene fluoride. It is a versatile engineering plastic with an outstanding balance of physical and chemical properties which qualify it for high performance service in a wide range of applications. It is a thermoplastic fluoropolymer capable of being fabricated in standard processing equipment. The molecular weight and molecular weight distribution have been carefully tailored to supply a grade suitable for a variety of processing requirements and end-use applications. KYNAR® 760 is suitable for the compression molding of block and extrusion of thick monofilaments and pipe. The powder form of this resin grade is available as KYNAR® 761 PVDF. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 to 1.79 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 76 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 44.8 to 55.2 | MPa | |
| Break, 23°C | 34.5 to 55.2 | MPa | |
| Tensile Elongation (Break, 23°C) | 20 to 100 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1380 to 2310 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 58.6 to 75.8 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 68.9 to 103 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 165 to 172 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (232°C, 100 sec^-1) | 2300 to 2900 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | 65% R.H. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 916VO-90 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Sylvin 9067-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ EXNL0357 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Ebalta AH 120 / TG | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| Keliren® CM421 | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |