VENYL SFC200
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sNmyPp_VENYL-SFC200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SFC200 is a 20% carbon fibre reinforced polyamide 6 lubrified intended for Injection moulding. APPLICATIONS VENYL SFC200 has been developed especially for demanding applications for good resistant final parts and rigidity combined with good stiffness and heat stabilization. Products requiring excellent combination between thermal and mechanical properties. VENYL SFC200 is available in black (VENYL SFC200). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.15 to 0.35 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 190 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 10700 | MPa | ISO 178 |
| Flexural Stress | 235 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 60 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 230 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+5 | ohms·cm | DIN 53482 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Nozzle Temperature | 255 to 275 | °C | |
| Mold Temperature | 85.0 to 100 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® RW2405 | Covestro - Polycarbonates | PC | Makrolon® |
| Sylvin 8469-53 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NYLOY® NS-0240N | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |
| Hostaform® WR140LG | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Moplen EP642S | PolyMirae | PP Impact Copolymer | Moplen |