LNP™ LUBRICOMP™ RX03643H compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sNiLCG_LNP-LUBRICOMP-RX03643H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RX03643H is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-R-03643 HC Product reorder name: RX03643H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.25 | g/cm³ | ASTM D792 |
| -- | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.0 to 1.2 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 to 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.79 | % | ISO 294-4 |
| Flow : 24 hr | 1.1 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.90 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5520 | MPa | ASTM D638 |
| -- | 5310 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 96.5 | MPa | ASTM D638 |
| Yield | 95.0 | MPa | ISO 527-2 |
| Break | 96.5 | MPa | ASTM D638 |
| Break | 95.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.4 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2 |
| Break | 2.4 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4830 | MPa | ASTM D790 |
| -- | 4500 | MPa | ISO 178 |
| Flexural Stress | 149 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.46 | ||
| vs. Itself - Static | 0.37 | ||
| Wear Factor - Washer | 159 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C 2 | 3.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 420 | J/m | ASTM D4812 |
| 23°C 3 | 28 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.90 | J | ASTM D3763 |
| -- | 2.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 256 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 252 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 239 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 221 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 4.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytech & Net VC910 | Polytech & Net Gmbh | EVA | Polytech & Net |
| POLYTROPE® STR 1060EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced TPO | POLYTROPE® |
| Anjacom® R250-H/GF30 | Almaak International GmbH | Nylon 6 | Anjacom® |
| ANYPOL SE-300LL | SH Energy & Chemical | PS (EPS) | ANYPOL |
| apinat® DP2091 | API SpA | Biodeg Polymers | apinat® |