Pearlthane® 15N95UV
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sMYp2u_Pearlthane-15N95UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PEARLTHANE® 15N95UV is a UV-resistant polyether copolymer based TPU, supplied in form of translucent, colourless pellets, combining hardness with excellent mechanical properties and excellent hydrolysis resistance. It can be extruded and injection-moulded. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.10 | g/cm³ | ASTM D792 |
| 20°C | 1.10 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 95 | ASTM D2240, ISO 868 | |
| Shaw D | 45 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 10.0 | MPa | ASTM D412, ISO 527 |
| 300% strain | 19.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 35.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 550 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 145 | kN/m | ASTM D624 |
| -- | 150 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 70 hr | 25 | % | ASTM D395B |
| 70°C, 22 hr | 40 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | -46.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 192 - 202 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 195 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 200 | °C | |
| Mold Temperature | 35.0 | °C | |
| Screw L/D Ratio | 23.0:1.0 |
| Injection instructions |
|---|
| Closing force: 30 tonsScrew diameter: 30 mmMaximum Hydraulic Pressure: 210 barMould: : Plaque 120x120x2 mmL/D ratio: : 23 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 185 - 200 | °C | |
| Cylinder Zone 2 Temp. | 200 - 230 | °C | |
| Cylinder Zone 3 Temp. | 210 - 230 | °C | |
| Cylinder Zone 4 Temp. | 200 - 220 | °C | |
| Die Temperature | 190 - 195 | °C |
| Extrusion instructions |
|---|
| Extruder Speed: 12 to 60 rpmCompression Ratio: 2:1 to 3:1L/D Ratio: 25:1 to 30:1 |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 10°C /min |
| 3 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aaroprene® ATPR 1000 70A | Aaron Industries Corp. | TPE | Aaroprene® |
| GERMAMID 6 HV GK 20 HKSZ UV | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| LNP™ VERTON™ MV006BS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |
| Pacrel® 5355N | Nanjing Jinling OPTA Polymer Co., Ltd. | TPE | Pacrel® |
| Wanthane® WHT-8885 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | Wanthane® |