Kingfa HG-542
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sLoUGt_Kingfa-HG-542.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa HG-542 is a polypropylene material, which contains a 25% filler. This product is available in North America or Asia Pacific,. The main features of Kingfa HG-542 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 1.3 - 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 70 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 1100 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 32.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20mm, injection molding | 45 | J/m | ASTM D256 |
| 23°C, 3.20mm, injection molding | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm, injection molding | 120 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm, injection molding | 65.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Filler Content, ISO3451/1, Method A: 25% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 400 HI SI 2 | RTP Company | PS (GPPS) | RTP |
| XANTAR® F 22 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| BMC T15(F) | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Hanwha Total PP GH42W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Hyundai EP PA6 LS460 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |