Order Products : sales@su-jiao.com
MAJORIS HT167 - 7759
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sKt8uh_MAJORIS-HT167---7759.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HT167 - 7759 is a mineral filled coloured polypropylene compound intended for injection moulding. The product is available in black (HT167 - 8229) and natural (HT167) but other colours can be provided on request. HT167 - 7759 has a easy flow very good processability, excellent surface quality and excellent long term UV-stability. APPLICATIONS HT167 - 7759 is intended for components, which require good surface quality and good impact.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 29 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.1 - 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1650 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 101 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 137 | °C | ISO 306/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AT0620GB | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| RTP 2740 U-70A | RTP Company | SBS | RTP |
| Flontech® FT-CAR15-8 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Hostacom TRC 452N G72828 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 2946-80 Clear 8422 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |