430GHU BK400 is a 30% glass fibre reinforced Nylon 6 compound that contains 2% carbon black by weight for robust outdoor weathering performance.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	heat stabilizer Carbon black (2%) UV stabilizer
Features	Light stabilization Good weather resistance Thermal Stability
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.35	g/cm³	ISO 1183
Molding Shrinkage ¹	0.30 - 0.80	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	2.1	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	8000	MPa	ISO 527-2
Tensile Stress	150	MPa	ISO 527-2
Tensile Strain (Break)	3.0	%	ISO 527-2
Flexural Modulus	7000	MPa	ISO 178
Flexural Stress	170	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	8.0	kJ/m²	ISO 180/A

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	> 200	°C	ISO 75-2/B
1.8 MPa, not annealed	200	°C	ISO 75-2/A

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	20	hr
Rear Temperature	250 - 280	°C
Middle Temperature	250 - 280	°C
Front Temperature	250 - 280	°C
Processing (Melt) Temp	250 - 290	°C
Mold Temperature	60.0 - 80.0	°C
Injection Rate	Fast
Back Pressure	Moderate
Screw Speed	Moderate

Injection instructions
No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	sKoAgI_Chemlon-430GHU-BK400.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TEREZ PA 6 7600 UV	TER HELL PLASTIC GMBH	Nylon 6	TEREZ PA 6
Biomer® P304	Biomer	Biodeg Polymers	Biomer®
ALTECH® PA6 A 4012/500 MR12	ALBIS PLASTIC GmbH	Nylon 6	ALTECH® PA6
Andur 9-5 APLF	Anderson Development Company	PUR-Ester/TDI	Andur
Axiall PVC 17870	Axiall Corporation	PVC, Flexible	Axiall PVC