LEXAN™ EXL1330 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sIHsPd_LEXANEXL1330resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1330 resin is a general purpose product available in a wide range of opaque colors and is an excellent candidate for a broad range of applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.40 - 0.80 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2100 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 58.6 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 61.4 | MPa | ASTM D638 |
| Fracture | 56.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Fracture 5 | 130 | % | ASTM D638 |
| Fracture | > 100 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2070 | MPa | ASTM D790 |
| -- 7 | 2100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 85.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 88.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 60 | kJ/m² | ISO 179/1eA |
| 23°C | 75 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -50°C | 590 | J/m | ASTM D256 |
| -30°C | 680 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 640 | J/m | ASTM D256 |
| -30°C 11 | 55 | kJ/m² | ISO 180/1A |
| 23°C 12 | 70 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C 13 | 1100 | J/m | Internal method |
| -30°C 14 | No Break | ISO 180/1U | |
| 23°C 15 | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 52.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 134 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 16 | 136 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 121 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 124 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 17 | 125 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ASTM D1525, ISO 306/B50 12 18 |
| -- | 145 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI | 120 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 850 | °C | IEC 60695-2-12 |
| 1.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 875 | °C | IEC 60695-2-13 |
| 3.00 mm | 875 | °C | IEC 60695-2-13 |
| Oxygen Index | 35 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 217 - 293 | °C | |
| Middle Temperature | 282 - 304 | °C | |
| Front Temperature | 293 - 316 | °C | |
| Nozzle Temperature | 288 - 310 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 71.0 - 93.0 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 249 - 288 | °C | |
| Cylinder Zone 2 Temp. | 243 - 271 | °C | |
| Cylinder Zone 3 Temp. | 227 - 254 | °C | |
| Adapter Temperature | 227 - 254 | °C | |
| Melt Temperature | 243 - 260 | °C | |
| Die Temperature | 238 - 260 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 48 hrsRoll Stack Temp - Bottom: 121 - 143 °CRoll Stack Temp - Middle: 82 - 127 °CRoll Stack Temp - Top: 77 - 116 °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | Double-Gated |
| 14 . | 80*10*3 |
| 15 . | 80*10*3 |
| 16 . | 120*10*4 mm |
| 17 . | 120*10*4 mm |
| 18 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP CESTILENE HD 1000 R | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| Selvol™ E 203 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| LNP™ STAT-KON™ KS000MXL compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |
| Sinpolene TPP6520 | Teknor Apex Asia Pacific PTE. LTD. | PP Copolymer | SINPOLENE |
| Durethan® BG 30 FN05 000000 | LANXESS GmbH | Nylon 6 | Durethan® |