Infino ASF-9810FM
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sHtWvP_InfinoASF9810FM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino ASF-9810FM is a polybutene terephthalate (PBT) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 60 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 1.5 - 1.8 | % | ASTM D955 |
| Transverse flow : 3.20mm | 1.7 - 2.0 | % | ASTM D955 |
| Lateral flow : 3.20mm | 1.7 - 2.0 | % | ISO 2577 |
| Traffic : 3.20mm | 1.5 - 1.8 | % | ISO 2577 |
| Water Absorption | |||
| Equilibrium, 23°C | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.40 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class m | 86 | ASTM D785 | |
| Class r | 116 | ASTM D785 | |
| R scale | 116 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 53.9 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 44.1 | MPa | ASTM D638 |
| Fracture | 49.0 | MPa | ISO 527-2/2 |
| Tensile Elongation | |||
| Fracture 4 | 50 | % | ASTM D638 |
| Fracture | 15 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2600 | MPa | ASTM D790 |
| -- 6 | 2320 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 83.4 | MPa | ASTM D790 |
| -- 8 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 29 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 34 | J/m | ASTM D256 |
| 23°C 10 | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 165 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed, 4.00mm | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 185 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 5.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 5.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS 7001 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| Tenite™ Acetate 105E2R30025 Natural, Trsp | Eastman Chemical Company | CA | Tenite™ Acetate |
| NYCOA Polyamide 1976 | Nycoa (Nylon Corporation of America) | Nylon 6 Alloy | NYCOA Polyamide |
| Grivory® HTV-6H1 black 9205 | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| Ryton® R-4-270NA | Solvay Specialty Polymers | PPS | Ryton® |