Rotec® ABS 1001
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Rotec® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sHMQN0_Rotec-ABS-1001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Rotec®ABS 1001 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in Europe and is processed by extrusion or injection molding. Rotec®The main characteristics of ABS 1001 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 49.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 15 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2700 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.18 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity ISO 8302, was tested in accordance with DIN 52612. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 210 - 250 | °C | |
| Middle Temperature | 210 - 250 | °C | |
| Front Temperature | 210 - 250 | °C | |
| Processing (Melt) Temp | < 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Screw rotation speed: moderate to highBack pressure: low to moderateInjection pressure: tool depending |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 190 - 210 | °C | |
| Cylinder Zone 2 Temp. | 190 - 210 | °C | |
| Cylinder Zone 3 Temp. | 190 - 210 | °C | |
| Cylinder Zone 4 Temp. | 190 - 210 | °C | |
| Cylinder Zone 5 Temp. | 190 - 210 | °C | |
| Melt Temperature | < 245 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® C33L 01 | BASF Corporation | Nylon 66/6 | Ultramid® |
| Nypol® PA A3 G30 HS UV PRTA011 NR395 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Elastamax™ HTE 1102 | PolyOne Corporation | SBC | Elastamax™ |
| EnCom T ABS 6050 | EnCom, Inc. | ABS | EnCom |
| OTECH ALLOY OTO9060LSZH - Riser Insulation | OTECH Corporation | TP, Unspecified | OTECH ALLOY |