Novodur® Ultra 4115
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Styrolution |
| Trademark: | Novodur® Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sGlBhx_Novodur-Ultra-4115.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novodur Ultra 4115 is a PC modified high heat injection molding grade. It provides extraordinary heat resistance combined with high impact strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 6.00 | cm³/10min | |
| 260°C/5.0 kg | 12.0 | cm³/10min | |
| Molding Shrinkage | 0.60 to 0.80 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 100 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2250 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 47.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 3.8 | % | |
| Break, 23°C | > 15 | % | |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 42 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 114 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 103 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 116 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 4.5E-3 | ||
| 1 MHz | 8.5E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 70.0 | °C | |
| Injection Velocity | 240 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Footwear GE-960F | S&E Specialty Polymers, LLC | PVC+NBR | S&E Footwear |
| Tecnoflon® FOR TF 838K | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| VICTREX® PEEK 450PF | Victrex plc | PEEK | VICTREX® PEEK |
| Karina GRAY COLOR CONCENTRATE 10/15-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYFLAM® RIPP 2000 E | A. Schulman Europe | PP Copolymer | POLYFLAM® |