Kynar Superflex® 2500-25
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Arkema |
| Trademark: | Kynar Superflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sGhqOK_Kynar-Superflex-2500-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KYNAR SUPERFLEX® 2500-25 is a pelletized, semi-crystalline VF2 based copolymer with a high Limiting Oxygen Index (LOI). KYNAR SUPERFLEX® 2500-25 is used for extrusion and injection molding applications where high flexibility and/or ductility is required along with extra flame and smoke resistance. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 to 1.82 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 50 to 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 11.7 to 19.3 | MPa | |
| Break, 23°C | 13.8 to 31.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 500 to 800 | % | ASTM D638 |
| Flexural Modulus (23°C) | 193 to 276 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 10.3 to 17.2 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 13.8 to 20.7 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 117 to 125 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (232°C, 100 sec^-1) | 500 to 1600 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | 65% R.H. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-G10-(color)-1 | Polymer Resources Ltd. | PC | PRL |
| Selvol™ 205 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| ELASTOSIL® R plus 4001/30 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| INEOS HDPE A4040 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| LNP™ THERMOCOMP™ WF008 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |