Generic Nylon 612 - Glass Fiber
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sGhhC3_Generic-Nylon-612---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 612 - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 - 1.46 | g/cm³ | ASTM D792 |
| 23°C | 1.17 - 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.19 - 0.52 | % | ASTM D955 |
| Transverse flow : 23°C | 0.90 - 2.0 | % | ASTM D955 |
| 23°C | 0.22 - 1.1 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.089 - 0.25 | % | ASTM D570 |
| Saturated, 23°C | 1.8 - 2.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.12 - 0.81 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 116 - 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3900 - 9740 | MPa | ASTM D638 |
| 23°C | 3000 - 12800 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 63.0 - 190 | MPa | ASTM D638 |
| Yield, 23°C | 63.0 - 121 | MPa | ISO 527-2 |
| Fracture, 23°C | 113 - 196 | MPa | ASTM D638 |
| Fracture, 23°C | 116 - 202 | MPa | ISO 527-2 |
| 23°C | 72.7 - 203 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.5 - 3.5 | % | ASTM D638 |
| Fracture, 23°C | 2.1 - 5.2 | % | ASTM D638 |
| Fracture, 23°C | 1.9 - 3.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3550 - 11400 | MPa | ASTM D790 |
| 23°C | 5690 - 11000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 120 - 272 | MPa | ASTM D790 |
| 23°C | 173 - 201 | MPa | ISO 178 |
| Compressive Strength (23°C) | 100 - 165 | MPa | ASTM D695 |
| Coefficient of Friction | 0.45 - 0.62 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.9 - 22 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 60 - 100 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 38 - 180 | J/m | ASTM D256 |
| 23°C | 6.4 - 17 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 240 - 1400 | J/m | ASTM D256 |
| 23°C | 17 - 79 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 5.97 - 10.5 | J | ASTM D3763 |
| 23°C | 1.81 - 3.08 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 199 - 221 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 208 - 217 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 194 - 217 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 188 - 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 208 - 215 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 209 - 213 | °C | |
| -- | 217 - 218 | °C | DSC |
| -- | 215 - 218 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 2.5E-5 - 4.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.0E-5 - 9.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral | 4.0E-5 - 1.6E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 3.9E-5 - 1.6E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.30 - 1.1 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+13 - 2.6E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 16 - 20 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 23°C | 3.40 - 4.02 | ASTM D150 | |
| 23°C | 3.95 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.013 - 0.020 | ASTM D150 | |
| 23°C | 0.014 - 0.065 | IEC 60250 | |
| Comparative Tracking Index | 598 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 675 - 700 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 700 - 725 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.5 - 82.7 | °C | |
| Drying Time | 3.0 - 4.1 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 259 - 270 | °C | |
| Middle Temperature | 265 - 269 | °C | |
| Front Temperature | 265 - 277 | °C | |
| Processing (Melt) Temp | 266 - 283 | °C | |
| Mold Temperature | 76.3 - 82.3 | °C | |
| Injection Pressure | 96.4 - 104 | MPa | |
| Back Pressure | 0.258 - 0.398 | MPa | |
| Screw Speed | 45 - 75 | rpm | |
| Cushion | 4.66 - 7.94 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 612 - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCA-4548 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| APEX® 3300-68NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Edgetek™ NN-30GF/000 | PolyOne Corporation | Nylon 66 | Edgetek™ |
| Karina GREEN PVC COMPOUND 602D40/ 93-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND 950-35/ 1-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |