PALBLEND®R 85 GF 10 is a polycarbonate + acrylonitrile butadiene styrene (PC + ABS) product, which contains a 10% glass fiber reinforced material. It is available in Europe. Typical application areas are: electrical/electronic applications. Features include: flame retardant/rated flame High stiffness

General Information
Filler / Reinforcement	Glass fiber reinforced material, 10% filler by weight
Features	Rigidity, high
Uses	Electrical/Electronic Applications
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)	15.0	cm³/10min	ISO 1133
Water Absorption			ISO 62
Saturated, 23°C	0.50	%	ISO 62
Equilibrium, 23°C, 50% RH	0.18	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	3750	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	62.5	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	3.0	%	ISO 527-2/1A/5

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	128	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	250	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Melt-Volume Flow Rate, ISO 1133, 260°C/5 kg: 10 to 20 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 3500 to 4000 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 60 to 65 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 4 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 126 to 129 °CDensity, ISO 1183: 1.18 to 1.2 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.4 to 0.6 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Additional Information

Melt-Volume Flow Rate, ISO 1133, 260°C/5 kg: 10 to 20 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 3500 to 4000 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 60 to 65 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 4 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 126 to 129 °CDensity, ISO 1183: 1.18 to 1.2 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.4 to 0.6 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Resin Grade	Manufacturer	Category	Trademark
VINIKA® T120D	Mitsubishi Chemical Performance Polymers, Inc.	PVC, Rigid	VINIKA®
Network Polymers HDPE 50 0753	Network Polymers, Inc.	HDPE	Network Polymers HDPE
ExxonMobil™ EnBA EN 33901	ExxonMobil Chemical	EnBA	ExxonMobil™ EnBA
Kepital® FL2010	Korea Engineering Plastics Co., Ltd	Acetal (POM) Copolymer	Kepital®
Sylvin 9993-65 Grey 9451	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin