Santoprene™ 241-55
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | Santoprene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sGVopz_Santoprene-241-55.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| It is a soft, colorable, special thermoplastic vulcanized elastomer (T PV) in the thermoplastic elastomer (TPE) series. It is suitable for the pipeline engineering field related to drinking water, and also suitable for food processing equipment. This brand of Sanduping TPV is a shear rate dependent product that can be processed on conventional thermoplastic injection molding or extrusion molding equipment. This is a polyolefin-based material that can be recycled in the production process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.958 | g/cm³ | ASTM D792 |
| -- | 0.960 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shaw A, 15 seconds, 23°C, 2.00mm) | 59 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow (100% Strain, 23°C) | 1.70 | MPa | ASTM D412, ISO 37 |
| Tensile Strength - Across Flow (Break, 23°C) | 4.50 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation - Across Flow (Break, 23°C) | 450 | % | ASTM D412, ISO 37 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RTI Elec | 100 | °C | UL 746 |
| RTI | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Resistance to Ignition (HVAR) | PLC 6 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Additional Information |
|---|
| 如果适用，这是基于扇形浇口注塑成型的平板测试结果。拉伸强度、伸长率和拉伸应力沿垂直流动方向测定 - ISO 1 型，ASTM die C。从埃克森美孚欧洲分支机构直接购买的所有产品都符合 REACH 法规。 对于埃克森 美孚未进口至欧洲的产品，用户应自行评估其是否满足 REACH 法规。 |
| Legal statement |
|---|
| 有关详细的产品监管信息，请联系客户服务。未经埃克森美孚化工书面允许，这种产品包括其产品名称，不得在任何医疗应用领域予以使用或 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 177 | °C | |
| Middle Temperature | 182 | °C | |
| Front Temperature | 182 | °C | |
| Nozzle Temperature | 188 - 221 | °C | |
| Processing (Melt) Temp | 193 - 232 | °C | |
| Mold Temperature | 10.0 - 51.7 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Clamp Tonnage | 4.1 - 6.9 | kN/cm² | |
| Cushion | 3.18 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 to 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 to 2.5:1.0 | ||
| Vent Depth | 0.025 | mm |
| Injection instructions |
|---|
| Santoprene TPV与乙缩醛和PVC不相容。更多关于加工和模具设计的信息，请查阅我们的《注射成型指南》。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Melt Temperature | 196 | °C | |
| Die Temperature | 199 | °C | |
| Back Pressure | 5.00 - 20.0 | MPa |
| Extrusion instructions |
|---|
| Santoprene TPV与乙缩醛和PVC不相容。更多关于加工和模具设计的信息，请查阅我们的《挤出成型指南》。 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA I XCF-0.3 | ROMPETROL PETROCHEMICALS S.R.L. | LDPE | MIDILENA I |
| SuperLite® SL550700-100 (1.5mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Vinnolit® K 707 E | Vinnolit GmbH & Co. KG | PVC Alloy | Vinnolit® |
| Hiprolon® 90 MNWHL G30 | Arkema | Nylon 612 | Hiprolon® |
| Hylex® P1025L1 | Entec Polymers | PC | Hylex® |