AKROTEK® PK-VM GF 30 natural (4706)
| Category: | PK-Aliphatic , Polyketone, Aliphatic |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROTEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sGPpla_AKROTEK-PK-VM-GF-30-natural-4706-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROTEK® PK-VM GF 30 natural (4706) is a 30% glass fibre reinforced Polyketon with high stiffness and strength and light inherent color. Applications are mainly components in mechanical engineering and the automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.48 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 98.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.40 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 0.60 to 0.70 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8000 | 7700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 115 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8200 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 165 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 12 | -- | kJ/m² | |
| -30°C | 12 | -- | kJ/m² | |
| 23°C | 15 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | 45 | -- | kJ/m² | |
| -30°C | 45 | -- | kJ/m² | |
| 23°C | 45 | 35 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 220 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPH2MF2-BLK | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| XYLEX™ X7300 resin | SABIC Innovative Plastics Asia Pacific | PC+Polyester | XYLEX™ |
| Bergamid™ B70 G25 NC025 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| CP PRYME® Polycarbonate PC100RULUV-18M BT Clear | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Ducor® DE3240UC | Ducor Petrochemicals BV | PP Random Copolymer | Ducor® |