NYCOA Polyamide ASN 27 250 KNF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sFgBNW_NYCOA-Polyamide-ASN-27-250-KNF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA ASN 27/250 KNF is a 25% glass fiber reinforced, heat stabilized, lubricated Nylon 6 resin used for injection molding. This material is specifically engineered for applications requiring high stiffness, toughness, dimensional stability, and a greater NYCOA ASN 27/250 KNF is available in UV stable, custom colors, and impact modified grades. It also has excellent chemical resistance to greases, oils, and other hydrocarbons. NYCOA ASN 27/250 KNF is suitable for injection molding and can be found in applications such as power tool housings and lawn & garden components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8050 | MPa | ASTM D638 |
| Tensile Strength 2 | 150 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 4 | 6930 | MPa | ASTM D790 |
| Flexural Strength 5 | 235 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 218 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 204 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 232 - 271 | °C | |
| Middle Temperature | 243 - 282 | °C | |
| Front Temperature | 254 - 291 | °C | |
| Nozzle Temperature | 252 - 291 | °C | |
| Processing (Melt) Temp | 254 - 291 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| 5 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene MCCPGL20 | Rainmaker Polymers LLC | PP Copolymer | Rainmaker Polypropylene |
| AKROLOY® PA GF 30 natural (3177) | AKRO-PLASTIC GmbH | Nylon 66+Nylon 6I/6T | AKROLOY® |
| Kepital® FW-24 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| LUBEMID B27 EL40 NATURAL | LUBEN PLAST srl | Nylon 6 | LUBEMID |
| Sylvin 8994-76 White 1367 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |