| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sEdmcK_SCHULAMID-66-GF-30-H-BLACK-REC.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| 30 % glass fibre reinforced PA 66, heat stabilized, recycled grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8800 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 130 | -- | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.2 | -- | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 240 | -- | °C | ISO 75-2/Af |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 2800-80A | RTP Company | TPO (POE) | RTP |
| Ultraform® N 2770 K | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| X-Pro SP 200 P 3081 | CTC Plastics, LLC | PP Copolymer | X-Pro |
| Karina IVORY PVC COMPOUND 800-35/ 2-BR-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kinta NB6015G | Kinta Technology (Hong Kong) Co., Ltd. | Nylon 6 | Kinta |