MBA PP 2131 F20
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | MBA Polymers |
| Trademark: | MBA PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sEYnQR_MBA-PP-2131-F20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A post-consumer recycled polypropylene copolymer with approximately 20% fillers. Available in standard black (reference 90/04). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 24.0 | MPa | ISO 527-2/50 |
| Flexural Modulus (23°C) | 2000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Melt Temperature | 180 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® TPU 1511 | Premix Oy | TPU, Unspecified | PRE-ELEC® |
| Scolefin 53 T 10-0 | Ravago Group | PP Homopolymer | Scolefin |
| TROSIFOL® UV+ | Kuraray Co., Ltd. | PVB | TROSIFOL® |
| Complet® LGF40-PA12 | PlastiComp, Inc. | Nylon 12 | Complet® |
| TECHNYL eXten® D 218CR V33 BLACK | Solvay Engineering Plastics | Nylon 66/610 | TECHNYL eXten® |