This data represents typical values that have been calculated from all products classified as: Generic CAP This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 - 1.21 | g/cm³ | ASTM D792 |
| 23°C | 1.19 - 1.21 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (210°C/2.16 kg) | 6.74 - 10.4 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 1.4 - 1.7 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 55 - 96 | ASTM D785 | |
| Ball Indentation Hardness | 56.0 - 65.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1290 - 1810 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 22.1 - 33.5 | MPa | ASTM D638 |
| Yield, 23°C | 30.0 - 40.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 27.4 - 41.4 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 4.0 | % | ISO 527-2 |
| Fracture, 23°C | 29 - 45 | % | ASTM D638 |
| Fracture, 23°C | 28 - 35 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 30 - 40 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1160 - 1860 | MPa | ASTM D790 |
| Flexural Strength | |||
| 23°C | 31.4 - 42.7 | MPa | ASTM D790 |
| 23°C | 39.4 - 45.0 | MPa | ISO 178 |
| Yield, 23°C | 29.0 - 55.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 - 30 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 240 - 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, annealed | 77.0 - 92.2 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 71.0 - 82.2 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 81.5 - 90.6 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 67.0 - 82.3 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 87.0 - 107 | °C | ASTM D1525 |
| -- | 86.0 - 96.5 | °C | ISO 306 |
| CLTE - Flow | 2.0E-5 - 2.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 - 1.0E+16 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 207 - 243 | °C | |
| Mold Temperature | 43.3 - 73.9 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic CAPThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® FT-1 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Unspecified | SILVER® |
| Tenac™ FS410 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Starpylen MX06023 | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| NatureFlex™ NP 165 | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| INSTRUC PPAGF20 | Infinity LTL Engineered Compounds | PPA | INSTRUC |