ALTECH® NXT PP-H A 2040/456.01 LE GF40 CP
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® NXT PP-H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sCa8oE_ALTECHNXTPPHA204045601LEGF40CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH®NXT PP-H A 2040/456.01 LE GF40 CP is a polypropylene homopolymer (PP Homopoly) product containing 40% glass fiber reinforcement. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Spiral Flow | |||
| -- 1 | 20.0 | cm | |
| -- 2 | 60.0 | cm | |
| Molding Shrinkage | ISO 294-4 | ||
| Lateral flow : 24 hours | 0.30 - 0.40 | % | ISO 294-4 |
| Traffic : 24 hours | 0.20 - 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 8250 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 8.0 | kJ/m² | ISO 179/1eA |
| -40°C | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | 45 | kJ/m² | ISO 179/1eU |
| -40°C | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 154 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 143 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Processing (Melt) Temp | 200 - 270 | °C | |
| Mold Temperature | 20 - 90 | °C |
| Note Message | |
|---|---|
| 1 . | 1 mm |
| 2 . | 2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ II210 | Polymics, Ltd. | PEI | Pyramid™ |
| SABIC® HDPE B5421 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Ebalta GM 725-7 / PUR 13 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| EPO-TEK® H77T | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LUBEMID B27 CM30 NATURAL | LUBEN PLAST srl | Nylon 6 | LUBEMID |