Asrene® SF 5007
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Chandra Asri Petrochemical |
| Trademark: | Asrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sCZ9H9_Asrene-SF-5007.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Asrene®SF 5007 is a high density polyethylene product,. It is available in North America, Europe or Asia Pacific. Asrene®SF 5007 applications include bags/linings, packaging, movies and industrial applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.050 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 15 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | > 500 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1100 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Elastic Modulus - MD (20 µm, Blown Film) | 850 | MPa | ASTM D882 |
| Elastic Modulus - TD (20 µm, Blown Film) | 1050 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 20 µm, blown film | 100 | MPa | ASTM D882 |
| TD : Broken, 20 µm, blown film | 55.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 20 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 20 µm, blown film | 700 | % | ASTM D882 |
| Dart Drop Impact (20 µm, Blown Film) | 130 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 20.0 µm | 6.9 | kN/m | ASTM D1922 |
| TD : 20.0 µm | 147.1 | kN/m | ASTM D1922 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (20.0 µm) | 34.3 | J/cm | ASTM D3420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 220 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 3 to 5 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A3 GF 30 SF SCHWARZ | A. Schulman Europe | PBT+ASA | SCHULADUR® |
| AKROMID® A3 GF 60 1 black (2395) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Crastin® S600F10 BK851 | DuPont Performance Polymers | PBT | Crastin® |
| Estane® AG 8451 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Hydrin® T3102 | Zeon Chemicals L.P. | Epoxy | Hydrin® |