STERLENE™ BMV203W
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | R&P (Pte.) Ltd. |
| Trademark: | STERLENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sCX97B_STERLENE-BMV203W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STERLENE™ BMV203W is a compound with high impact, UV stabilized. This product is designed for automotive exterior applications like bumpers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 24 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1860 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield, 23°C) | 18.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 8.9 | % | |
| Break, 23°C | 350 | % | |
| Flexural Modulus 2(23°C) | 1570 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 26.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -30°C, Complete Break | 6.3 | kJ/m² | |
| 23°C, Partial Break | 50 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Complete Break | 6.1 | kJ/m² | |
| 23°C, Partial Break | 60 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 51.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V72G | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| BESTNYL SE30VI02AWXL | Triesa Plastics | Nylon 66 | BESTNYL |
| Karina GRAY PVC COMPOUND 105900-18/121-B-ACE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ RFL26S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Sylvin 4200-88 Clear Green 3213 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |