Fiberfil® J-60/40/E8
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sCPxrK_Fiberfil-J-60-40-E8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®J-60/40/E8 is a polypropylene homopolymer (PP Homopoly) material, and the filler is 40% glass fiber reinforced material. This product is available in North America,. Fiberfil®The main features of J-60/40/E8 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.20 | % | ASTM D955 |
| 6.35 mm | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7580 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 93.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 6890 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 121 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 157 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 152 | °C | ASTM D648 |
| Additional Information |
|---|
| Rockwell Hardness, ASTM D785, R-Scale: 100 to 110 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 CI2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Titacon® CW901 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Baoding 68T80 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| DILAMID® 6 FV NATURAL 2802 SR | Dilaplast S.p.A. | Nylon 6 | DILAMID® |
| LUCITE® 47G | Lucite International Inc. | Acrylic (PMMA) | LUCITE® |