RTP 200H TFE 10 SI 1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sC0lGn_RTP-200H-TFE-10-SI-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ASTM D638 |
| Tensile Strength | 36.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 1380 | MPa | ASTM D790 |
| Flexural Strength | 55.2 | MPa | ASTM D790 |
| Compressive Strength | 30.3 | MPa | ASTM D695 |
| Coefficient of Friction (With Metal-Dynamic) | 0.10 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 210 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.35 mm) | 1200 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 216 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 82.2 | °C | ASTM D648 |
| CLTE - Flow | 8.1E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.26 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.015 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 20mil/in.Flammability, ASTM D-635: B in/min.Wear Factor, K, ASTM D-3702: 30E-10in³/min/ft/lb/hrCoefficient of Friction, Dynamic, ASTM D-3702: 0.10The wear factor and dynamic coefficient of friction were both tested on thrust washer apparatus at 300 FPM, 8500 PV, against 1141 Ryex steel of hardness 18-22 Rockwell C, 12-16 micro smoothness. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 282 - 296 | °C | |
| Middle Temperature | 282 - 296 | °C | |
| Front Temperature | 282 - 296 | °C | |
| Mold Temperature | 65.6 - 107 | °C | |
| Injection Pressure | 103 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDM 520 | Marco Polo International, Inc. | HDPE | MARPOL® |
| RTP 156 | RTP Company | PP Copolymer | RTP |
| TECHLEN M2302HK | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Arak LLDPE LL0209CA | Shazand (Arak) Petrochemical Corporation | LLDPE | Arak LLDPE |
| Arnitel® EM631 | DSM Engineering Plastics | TPC-ET | Arnitel® |