AKROMID® B3 GF 30 1 blue (5350)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sBSYu6_AKROMIDB3GF301blue5350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 30 1 blue (5350) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength Applications are mainly components in mechanical engineering and in the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 66.0 | -- | cm | Internal method |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.70 | -- | % | ISO 294-4 |
| Flow | 0.30 | -- | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 6.3 - 6.9 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 2.1 - 2.3 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 230 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 170 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 5.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8500 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 270 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 80 | 100 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 150 | -- | °C | ISO 75-2/C |
| Melting Temperature 3 | 220 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.8 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.6 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide R1000HI620 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| AKROMID® B3 GF 40 black (3383) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Sylvin 83046-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| MARPOL® LL6R 802 | Marco Polo International, Inc. | LLDPE | MARPOL® |
| Sylvin 3250-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |