Akulon® S225-KS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sBNakW_AkulonS225KS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon®S225-KS is a polyamide 66 (nylon 66) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. Akulon®The main features of the S225-KS are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4000 | 1700 | MPa | ISO 527 |
| Tensile Stress (Yield) | 85.0 | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | 20 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 12 | 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 | |||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2 |
| 1.8 MPa, not annealed | 90.0 | -- | °C | ISO 75-2 |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.4E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 2.80 | 7.00 | IEC 60250 | |
| 1 MHz | 3.30 | 3.80 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 8.5E-3 | 0.14 | IEC 60250 | |
| 1 MHz | 0.012 | 0.090 | IEC 60250 | |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.38 mm | V-0 | -- | IEC 60695-11-10, -20 | |
| 0.75 mm | V-0 | -- | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | -- | IEC 60695-11-10, -20 | |
| Oxygen Index | 36 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 260 - 270 | °C | |
| Front Temperature | 265 - 275 | °C | |
| Nozzle Temperature | 260 - 265 | °C | |
| Processing (Melt) Temp | 265 - 275 | °C | |
| Mold Temperature | 50 - 80 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 - 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SGN4029 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Elastron® D P.D100.A50.N | Elastron USA, Inc. | SBS | Elastron® D |
| Huafon HF-3060D | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Iupilon® GSH2050DF | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| CP PRYME® Nylon 66 NN333HSL BK | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |