Sarlink® TPV 4755B42
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sBBbtd_Sarlink-TPV-4755B42.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink® TPV 4755B42 is a Thermoplastic Vulcanizate (TPV) material. It is available in Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.908 | g/cm³ | ASTM D792 |
| -- | 0.910 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A, 5 sec, Extruded | 54 | ||
| Shore A, 5 sec, Injection Molded | 56 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Across Flow : 100% Strain | 1.80 | MPa | |
| Flow : 100% Strain | 2.70 | MPa | |
| Tensile Strength | ASTM D412, ISO 37 | ||
| Across Flow : Break | 5.00 | MPa | |
| Flow : Break | 4.30 | MPa | |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Across Flow : Break | 500 | % | |
| Flow : Break | 390 | % | |
| Tear Strength - Across Flow | |||
| -- | 19.3 | kN/m | ASTM D624 |
| -- 1 | 19 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 19 | % | |
| 70°C, 22 hr | 28 | % | |
| 125°C, 70 hr | 43 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | |||
| 135°C, 1000 hr | -2.0 | % | ASTM D573, ISO 188 |
| 100% Strain, 135°C, 1000 hr | 7.0 | % | ASTM D573 |
| 150°C, 168 hr | -6.0 | % | ASTM D573, ISO 188 |
| 100% Strain, 150°C, 168 hr | -1.0 | % | ASTM D573 |
| 100% Strain 135°C, 1000 hr | 7.0 | % | ISO 188 |
| 100% Strain 150°C, 168 hr | -1.0 | % | ISO 188 |
| Change in Ultimate Elongation in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | -4.0 | % | |
| 150°C, 168 hr | -2.0 | % | |
| Change in Durometer Hardness in Air | ASTM D573, ISO 188 | ||
| Shore A, 135°C, 1000 hr | 2.0 | ||
| Shore A, 150°C, 168 hr | -2.0 | ||
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 90 | % | ASTM D471, ISO 1817 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity | |||
| Capillary : 200°C | 220 | Pa·s | ASTM D3835 |
| Capillary @ 206/s : 200°C | 220 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 177 to 216 | °C | |
| Middle Temperature | 177 to 216 | °C | |
| Front Temperature | 177 to 216 | °C | |
| Nozzle Temperature | 188 to 221 | °C | |
| Processing (Melt) Temp | 182 to 232 | °C | |
| Mold Temperature | 10.0 to 65.6 | °C | |
| Back Pressure | 0.0689 to 1.03 | MPa | |
| Screw Speed | 100 to 200 | rpm | |
| Screw L/D Ratio | 25.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVADURAN® 5010GN1-30AM2 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| ARCEL® ULV (4.00 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| ICORENE® 3935 | ICO Polymers SA, A Division of A. Schulman | PE Copolymer | ICORENE® |
| OmniTech™ ABS GR10 | OMNI Plastics, LLC | ABS | OmniTech™ |
| Sylvin 83048-85 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |