MELOPAS® MP 6605

Category:	Mel Phenolic , Melamine Phenolic
Manufacturer:	RASCHIG GmbH
Trademark:	MELOPAS®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	sB4gO3_MELOPAS-MP-6605.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Cellulose reinforced Melamine moulding compound

Very good electrical properties, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability, good gliding behaviour

Primary application(s): Moulded parts in electrical engineering, arc chambers

This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS)

General Information
Filler / Reinforcement	Cellulose
Features	Good Electrical Properties Good Strength Good UV Resistance Good Wear Resistance High Hardness Medium Heat Resistance
Uses	Electrical Parts
Agency Ratings	EU 2002/96/EC (WEEE) EU 2006/122/EC
RoHS Compliance	RoHS Compliant
Forms	Granules
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.50 to 1.70	g/cm³	ISO 1183
Apparent Density	0.55 to 0.75	g/cm³	ISO 60
Molding Shrinkage - Flow ¹	0.80 to 1.2	%	ISO 2577
Water Absorption (23°C, 24 hr)	< 2.0	%	ISO 62
Post Shrinkage ²	1.2 to 1.8	%	ISO 2577

Thermal	Nominal Value	Unit	Test Method
Maximum Service Temperature			IEC 60216
<50 h	160	°C
20,000 h	135	°C

Additional Information	Nominal Value	Unit
Compression Molding Molding Pressure	> 20.0	MPa
Compression Molding Temperature	160 to 180	°C

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Injection Molded)	5000 to 8000	MPa	ISO 527-2
Tensile Stress (Injection Molded)	60.0 to 85.0	MPa	ISO 527-2
Flexural Modulus (Injection Molded)	6000 to 8000	MPa	ISO 178
Flexural Stress (Injection Molded)	90.0 to 110	MPa	ISO 178
Compressive Stress	200 to 250	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (Injection Molded)	1.3 to 2.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (Injection Molded)	7.0 to 11	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, Unannealed	155 to 180	°C	ISO 75-2/A
8.0 MPa, Unannealed	110 to 130	°C	ISO 75-2/C
CLTE - Flow (50 to 100°C)	1.5E-5 to 3.5E-5	cm/cm/°C	ISO 11359-2
Thermal Conductivity	0.40 to 0.50	W/m/K	ASTM E1461

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+10 to 1.0E+11	ohms	IEC 60093
Volume Resistivity	1.0E+11 to 1.0E+12	ohms·cm	IEC 60093
Electric Strength	20 to 25	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	16.0 11.0
1 MHz	9.00 7.00
Dissipation Factor			IEC 60250
100 Hz	0.30 to 0.50
1 MHz	0.030 to 0.050
Arc Resistance	PLC 5		ASTM D495
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm, Tested by RASCHIG)	V-0		UL 94
Glow Wire Flammability Index	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature	900	°C	IEC 60695-2-13

Injection	Nominal Value	Unit
Middle Temperature	70.0 to 90.0	°C
Front Temperature	90.0 to 100	°C
Processing (Melt) Temp	100 to 115	°C
Mold Temperature	160 to 180	°C
Back Pressure	0.800 to 1.20	MPa
Screw Speed	80 to 120	rpm

Note Message
1 .	Injection Molded
2 .	168 h / 110°C

Resin Grade	Manufacturer	Category	Trademark
RAYPRENE® NB223-S4006	R&P (Pte.) Ltd.	TPE	RAYPRENE®
SEETEC LDPE XL610	Lotte Chemical Corporation	LDPE	SEETEC LDPE
Trademark PP PPC2040M	Trademark Plastics Corporation	PP Impact Copolymer	Trademark PP
XANTAR® F 22 R	Mitsubishi Engineering-Plastics Corp	PC	XANTAR®
CYCOLAC™ X11-NH resin	SABIC Innovative Plastics Asia Pacific	ABS	CYCOLAC™