Order Products : sales@su-jiao.com
CYCOLOY™ C7210A resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sB4VLT_CYCOLOY-C7210A-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cycoloy* C7210A resin is talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications. Very good modulus-ductility balance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.40 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3520 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 63.4 | MPa | |
| Break | 49.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 3.6 | % | |
| Break | 80 | % | |
| Flexural Modulus 4(50.0 mm Span) | 3140 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 106 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 180 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1900 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 47.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 92.2 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 82.2 | °C | |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 6 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 5.9E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.7E-5 | cm/cm/°C | |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 85.0 | °C | UL 746 |
| RTI Str | 90.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.19 mm | V-0 | ||
| 1.98 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 221 to 254 | °C | |
| Middle Temperature | 221 to 266 | °C | |
| Front Temperature | 243 to 277 | °C | |
| Nozzle Temperature | 243 to 277 | °C | |
| Processing (Melt) Temp | 243 to 277 | °C | |
| Mold Temperature | 60.0 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WINTEC™ WFX4TA | Japan Polychem Corporation | PP Random Copolymer | WINTEC™ |
| Xuchuan XCG-100 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| VAMPSAB 0023 V2 DF | Vamp Tech | PS (GPPS) | VAMPSAB |
| Karina LILAC PVC COMPOUND 831-34/148-IS RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sumiliteresin® ECP-296 | SBHPP | Epoxy | Sumiliteresin® |