Pebax® Rnew 80R53 SP 02
| Category: | PEBA-Ether , Polyether Block Amide |
| Manufacturer: | Arkema |
| Trademark: | Pebax® Rnew |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sAtKeu_Pebax-Rnew-80R53-SP-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyether block amide Pebax® Rnew 80R53 SP 02 is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV resistant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.70 | % | |
| Equilibrium, 23°C, 50% RH | 0.80 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 73 | ||
| Shore D, 15 sec | 67 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Flexural Modulus | 850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 16 | kJ/m² | |
| 23°C | 43 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 188 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Renewable Carbon Conent | 93 to 97 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 5.0 to 7.0 | hr | |
| Processing (Melt) Temp | 230 to 290 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 5.0 to 7.0 | hr | |
| Melt Temperature | 230 to 290 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEO-ZEX™ 0134N | Prime Polymer Co., Ltd. | LLDPE | NEO-ZEX™ |
| BRALEN® NA 7-25 | Slovnaft Petrochemicals, s.r.o. | LDPE | BRALEN® |
| CoolPoly® D4302 | Celanese Corporation | TPC-ET | CoolPoly® |
| Hifax TRC770PHS | LyondellBasell Industries | TPO (POE) | Hifax |
| Petro Rabigh PE FS150A | Rabigh Refining & Petrochemical Co. | LLDPE | Petro Rabigh PE |