PALBLEND® R 85 Datasheet,PC+ABS,pal plast GmbH-SHANGHAI SUSHENG

Message
PALBLEND®R 85 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in Europe. PALBLEND®R 85 applications include electrical/electronic applications and the automotive industry. Features include: flame retardant/rated flame Good dimensional stability Impact resistance

General Information
Features	Good dimensional stability Impact resistance, high
Uses	Electrical/Electronic Applications Car interior parts
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.14	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)	25.0	cm³/10min	ISO 1133
Water Absorption			ISO 62
Saturated, 23°C	0.60	%	ISO 62
Equilibrium, 23°C, 50% RH	0.18	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2200	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	52.5	MPa	ISO 527-2/1A/50
Tensile Strain (Yield, 23°C)	5.0	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break (23°C)	50	%	ISO 527-2/1A/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	38	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	128	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	250	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Melt-Volume Flow Rate, ISO 1133, 260°C/5 kg: 20 to 30 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2100 to 2300 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 50 to 55 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 4 to 6 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 35 to 40 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 126 to 129 °CDensity, ISO 1183: 1.13 to 1.15 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.5 to 0.7 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Additional Information

Melt-Volume Flow Rate, ISO 1133, 260°C/5 kg: 20 to 30 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2100 to 2300 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 50 to 55 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 4 to 6 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 35 to 40 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 126 to 129 °CDensity, ISO 1183: 1.13 to 1.15 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.5 to 0.7 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Resin Grade	Manufacturer	Category	Trademark
POLYPRO® 5014L AB305	YUHWA Korea Petrochemical Ind. Co., Ltd.	PP Homopolymer	POLYPRO®
Sarlink® TPE ML-2355B	Teknor Apex Company	TPE	Sarlink® TPE
Elastron® V V201.A78.B	Elastron USA, Inc.	TPV	Elastron® V
PermaStat PLUS® 4500	RTP Company	PK	PermaStat PLUS®
Starex HG-0760TV	LOTTE ADVANCED MATERIALS CO., LTD.	ABS	Starex

Category:	PC+ABS , Polycarbonate + ABS
Manufacturer:	pal plast GmbH
Trademark:	PALBLEND®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	sAoiHb_PALBLEND-R-85.pdf