Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 403 SP is a 20% glass fiber polystyrene designed for use in foam molding. It is designed for molding with the nitrogen or chemical blowing agent process. Values shown are foamed to a 20% density reduction. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6210 | MPa | ASTM D638 |
| Tensile Strength | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 5520 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 80 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 82.2 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 76.7 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | HB | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, ASTM D955, 0.25in: 1 mil/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 204 - 288 | °C | |
| Middle Temperature | 204 - 288 | °C | |
| Front Temperature | 204 - 288 | °C | |
| Mold Temperature | 37.8 - 71.1 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 50 - 90 | rpm | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® X7010 | Vyncolit N.V. | Phenolic | Vyncolit® |
| CoREZYN® CORVE8180 | Interplastic Corporation | Vinyl Ester | CoREZYN® |
| Durez® 32543 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| LNP™ STAT-KON™ DEL339XF compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Sylvin 9604-90 Grey 9132 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |