LNP™ THERMOCOMP™ PX01658 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sA4L0m_LNP-THERMOCOMP-PX01658-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP PX01658 is a compound based on Nylon 6 containing Proprietary Fillers. Also known as: LNP* THERMOCOMP* Compound PDX-P-01658 Product reorder name: PX01658 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.75 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 32700 | MPa | ASTM D638 |
| -- | 30900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 257 | MPa | ASTM D638 |
| Break | 267 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 2.0 | % | ISO 527-2/5 |
| Break 3 | 2.0 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 24700 | MPa | ASTM D790 |
| -- 5 | 25800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 393 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 392 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 391 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 8 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 9 | 68 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.0 | J | ASTM D3763 |
| -- | 3.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 220 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 213 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 210 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYNE® Olefins W6403 | Tyne Plastics LLC. | PP, Unspecified | TYNE® Olefins |
| Nipol® SBR 1723 | Zeon Corporation | SBR, Emulsion | Nipol® SBR |
| DJSilicone NE-9170 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Geon™ Vinyl Flexible A8501 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Sylvin 2900-60 Clear Pink 6310 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |