Order Products : sales@su-jiao.com
HiFill® PA4/6 0206
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s9Nn6U_HiFill-PA4-6-0206.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PA4/6 0206 is a Polyamide 46 (Nylon 46) product. It can be processed by injection molding and is available in North America. Primary characteristic: conductive. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 10300 | MPa | ASTM D790 |
| Flexural Strength | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 291 | °C | |
| 1.8 MPa, Unannealed | 277 | °C | |
| CLTE - Flow | 3.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.98 | W/m/K | ASTM C177 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® RS 32CG20HSL BK409 | DuPont Performance Polymers | Nylon 610 | Zytel® RS |
| Axiall PVC 1702 Clear 7070 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Fainplast PVC PG 83 | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| LEXAN™ 923X resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| POLIMAXX 320PC | IRPC Public Company Limited | SAN | POLIMAXX |