Grivory® GVL-4H nat
| Category: | Nylon 66+Nylon 6I/X , Polyamide 66 + PA 6I/X |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grivory® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s9Ltzp_Grivory-GVL-4H-nat.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grivory® GVL-4H nat is a Polyamide 66 + PA 6I/X (Nylon 66+Nylon 6I/X) material filled with 40% long glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion or injection molding. Important attributes of Grivory® GVL-4H nat are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.40 | -- | % | |
| Flow | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.6 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.4 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 255 | 230 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 14000 | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 240 | 205 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 2.6 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 30 | 30 | kJ/m² | |
| 23°C | 30 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | 75 | kJ/m² | |
| 23°C | 85 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 210 | -- | °C | ISO 75-2/C |
| Continuous Use Temperature | Internal Method | |||
| -- 1 | 100 to 120 | -- | °C | |
| -- 2 | 220 | -- | °C | |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 33 | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA66+PA6I/X, MH, 14-140, GF40 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen H30S | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| ALCOM® PC 740/4 UV WT1370-07LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| EVATHENE® UE647-04 | USI Corporation | EVA | EVATHENE® |
| Hypro® PPH-GF10 NATURAL | Entec Polymers | PP Homopolymer | Hypro® |
| ISPLEN® PR 299 C1M | REPSOL | PP Random Copolymer | ISPLEN® |